Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Ready-to-Use Product Features
- Product Highlights
- AT-804030 is a 1:1, meter-mix, methacrylate-based structural adhesive formulated to bond engineered thermoplastics,thermosets, composites, and metal structural elements in any combination.
- It has excellent adhesion to as-received metalsurfaces, including aluminum, galvanized, stainless and plated steels.
- It exceeds the strength of PVC, ABS, acrylic,polycarbonate, fiberglass and many other composites and engineering plastics.
- It forms tough, high-strength bonds withoutsurface preparation, primers, or chemical wipes.
- It features a 3-4 minute open time for fast fixturing.
- This product is formulated asa non-sag, high viscosity product with a special filler for holding anchoring studs and clips to walls and ceilings and is easilydispensed from cartridges with static mixer tubes. AT-804030 also provides low temperature impact and peel strength.
- This formulation is Reach Compliant and acid free.
- Substrate : Almost all substrates (except low energy & rubber)
- Non-slide General Purpose Bonder 30 ml cartridge. Seal cap included.
Applications & Uses
- Compatible Substrates & Surfaces
Properties
- Color (Properties)
- Mechanical Properties
Value Units Test Method / Conditions Peel Strength (Steel, at 0.432 mm Gap) 11.4 N/mm ASTM D 1876 Impact Strength (Aluminum, 2 kg Hammer) 9.6 KJ/m² GM9751P Tensile Shear (Steel, After 24 Hours Cure) 22.0 N/mm² ASTM D1002 Tensile Shear (Aluminum, After 24 Hours Cure) 22.4 N/mm² ASTM D1002 Tensile Shear (Galvanized, After 24 Hours Cure) 15.2 N/mm² ASTM D1002 Tensile Shear (Steel, After 1 Hours Cure (Approx 75% full cure)) 16.6 N/mm² ASTM D1002 Tensile Shear (Aluminum, After 1 Hours Cure (Approx 75% full cure)) 16.7 N/mm² ASTM D1002 Tensile Shear (Galvanized, After 1 Hours Cure (Approx 75% full cure)) 12.4 N/mm² ASTM D1002 - Uncured Properties
Value Units Test Method / Conditions Brookfield Viscosity (Part A, TD at 2.5 rpm) 250000.0 cPs - Brookfield Viscosity (Part B, TD at 2.5 rpm) 350000.0 cPs - Brookfield Viscosity (Part A, TD at 20 rpm) 50000.0 cPs - Brookfield Viscosity (Part B, TD at 20 rpm) 90000.0 cPs - Density (Part A) 8.82 pounds/gallon - Density (Part B) 8.45 pounds/gallon - Mix Ratio 1:1 Weight & Volume - Flashpoint 11.0 °C - - Typical Cured Properties
Value Units Test Method / Conditions Hardness (Shore D) 68 - 70 - - Elongation 10.0 % - Operating Temperature - 40 to 125 °C - Brookfield Viscosity (Mixed, TD at 2.5 rpm) 265000.0 cPs - Brookfield Viscosity (Mixed, TD at 20 rpm) 65000.0 cPs - Density (Mixed) 8.63 pounds/gallon - Working Time 3 - 4 Minutes - Fixture Time (3 kg weight, Aluminum/ Aluminum) 5 - 6 Minutes - Peak Exotherm Temperature (Range) 125 to 135 °C - Peak Exotherm Time (Range) 12 - 14 Minutes - - Chemical Resistance
- AT-804030 exhibits good resistance to commonly encountered service environments and chemicals.
- Resistance to specific chemicals and environments must be tested by the end-user to ensure theadhesive is compatible to both the substrate and the environment.
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Packaging Information
AT-804030 is available in 30 ml.
Storage & Handling
- Shelf Life
- 6 months (in original sealed bulk containers), 12 months (in cartridges)
- Storage Conditions
- The materials can be used with conventional meter/mix dispenseequipment.
- All materials should be stored in a cool place when not used for an extended period of time.
- Do not freeze.