- Weld Mount AT-2010 is a high performance two part methacrylate adhesive engineered to bond a wide range of plastics, metalsand composite assemblies.
- It offers outstanding bond strength, is extremely durable, with excellent impact and weathering properties.
- It is a unique adhesive which has very high viscosity to hold Weld Mount parts in position without sagging and it’s 5minute fixture time makes it ideal for production applications.
- 75% of the ultimate strength is achieved in 15 - 20 Minutes.
- Fullstrength is reached in 24 hours.
- AT-2010 greatly increases the reliability of finished assemblies with , it’s ability to withstandextreme temperature fluctuation and thermal cycling, and resistance to a wide range of chemicals and environmental conditions
- Substrate : Fiberglass
- Ideal for a fastpaced work environment
- Dispense Gun : AT-300
- Static Mix tip : AT-850 3.25" Mix Tip
- AT-2010 bonds to:
- Metals: Aluminum, Steel, Stainless, steel, Coated metals
- Thermo sets: Fiberglass, Phenolics, Gel coats, Epoxy, Rim Urethane, Polyurethane, Liquid molding resins, SMC
- Thermo plastics: Acrylics, ABS, Polycarbonates, Nylons, PPOs, Vinyl's, PVC's, Styrene's, Peek's, PBT Blends, PET Blends
- Gap filling to .375"
- Little surface prep
- Excellent strength
- Impact resistant
- 100% reactive
- Room temperature cure
- Easily applied
Applications & Uses
- Compatible Substrates & Surfaces
- Cleaning Information
- It is important to remove excessadhesive from the substrate before itis cured.
- Solvent cleaners such as alcohol or MEK yield good results.
- Once the adhesive has cured it will bevery difficult to remove and mayrequire as much as 350° F to soften to allow removal.
- Mixing
- It is highly recommended that either meter mix equipment or cartridges with static mix nozzles be used toproperly ratio and dispense the adhesive.
- For hand mixing, combine Part A and Part B in the correct ratioand mix thoroughly.
- Heat buildup during and after mixing is normal.
- To reduce the likelihood of exothermic reaction or excessive heat buildup, mix less than 100 grams at a time.
- Mixing smalleramounts will minimize heat buildup.
- Bonding
- For optimum bond strength and to insure maximum performance in the finished assembly mate parts together within the specified working time of the adhesive (3—4 Minutes).
- Made sure the bond joint has uniform coverage and that a sufficient amount of adhesive is in the bond area.
- It is important to have theadhesive applied, parts aligned and positioned, within the established work time for the product.
- To ensure maximum performance in the finished assembly parts should remain undisturbed until the joint issufficiently cured.
- For the highest strength bonds surfaces should be clean, dry, and free of contamination.
- Extensive surface preparation is not required for AT-2010 and good bonds can be formed on most substrates after a solvent wipe.
- However we recommend that metal surfaces (particularly aluminum) be given a scotch brite cleaning to remove surface oxidation to achieve the highest bond strengths.
Properties
- Physical Properties of Cured Material
Value Units Test Method / Conditions Shear Strength (Steel) 2,600 - 3,500 psi - Tensile Strength (Steel) 3,800 - 4,000 psi - Working Time 3 to 4 Minutes - Handling Strength (for 75% overall strength) 20.0 Minutes - Gap Fill 0.375 Inch - Temperature Range - 65 to 225 °F - Peak Exotherm (at 75°F) 280.0 °F - - Uncured Properties
Value Units Test Method / Conditions Viscosity (Resin, at 25°C) 85,000 - 125,000 cps - Viscosity (Activator, at 25°C) 85,000 - 125,000 cps - Mixed Ratio 1:1 Weight & Volume - Specific Gravity 1.04 - - Flash Point 58.0 °F - - Effect of Temperature
- AT-2010 is best used at temperatures between 65° F and 80° F.
- Temperatures below 65° F will slow the cure speed of the material and theviscosities will be higher.
- Temperatures above 80° F will cause the material to cure faster and the viscosities will be lower.
Packaging & Availability
- Packaging Type
- Packaging Information
AT-2010 is conveniently packaged in 50 Ml cartridges.
Storage & Handling
- Shelf Life
- 12 months
- Storage Conditions
- The shelf life of AT-2010 is one yearfrom the date of manufacture which is indicated on the cartridge when refrigerated at 40 degrees F.
- Shelf lifeis 6 months from the date of manufacture when the product isstored properly at a temperature nogreater than 72° F.
- Exposure totemperatures above 72 F will reduce the shelf life of the product.
- AT-2010 should never be frozen.
- AT-2010 is flammable.
- Keep it away from heat,sparks and open flames.