Swift®col 2607-2A

Identification

Chemical Family

Polyurethanes (PU)

GBU

EA

RTU Product Type

2K (2 component) Adhesive,

Solventborne Adhesive

Categories

Markets → Automotive & Transportation → Applications → Automotive → Interior

Technologies → Adhesives & Sealants → Product Families → Bonding Technology → 2K Liquid Reactive Adhesives

Technologies → Adhesives & Sealants → Product Families → Bonding Technology → Solvent-Based Reactive Adhesives

Applications

Application Area

Automotive Interior Trim,

Lamination,

Press Lamination,

Vacuum Lamination,

Membrane Lamination,

Automotive Applications,

Transportation Application

Application Method

Brush,

Spray

Compatible Substrates & Surfaces

Leather,

Textiles,

Wood,

Polycarbonate (PC),

Acrylonitrile Butadiene Styrene (ABS),

Artificial Leather,

Pre-treated Olefins,

Sheet Molding Compound (SMC),

Polyethersulfone (PES),

Polyvinyl Chloride (PVC) Film

Applications & Uses

Application Guidelines

• Flammable - Product is flammable. Keep away from flame and heat
• Safety - Formation of carbon dioxide can result in dangerous increase of pressure
• Storage - All swift®col hardeners (Part B) react with water to carbon dioxide and insoluble urea. Therefore, all containers must always be kept sealed tightly. Penetration of water in any form must be avoided.
• Preparation - The components must be mixed thoroughly until the mixture shows a uniform color.
• Frost protection - Protect Swift®col 2607-2A strictly from frost, product will be damaged.

Cleaning Information

• General Instructions - Cured adhesive can only be removed mechanically. 
• Cleaner for Tools - Helmitin® 683 and Helmitin® 694

Drying Information

• Recommended drying temperature (as specified in Technical Data section) depends on part size and coating weight.
• Caution: The drying time is influenced by the absorbency of the surface, drying temperature and coating weight and needs to be checked under real life conditions.

Processing Information

• Suitable Substrates - Polyvinyl chloride films, Thermoplastic polyolefin foil, Artificial leather, Pretreated olefines, Acrylonitrile butadiene styrene, Polycarbonate, Polyester, Sheet moulding compound, Leather, Textile, Wood based materials
• Surface Requirements - Minimum surface tension 40 mN/m, dry, clean, free of grease, free of dust, free of oil
• Application Method - Brushing, Automatic application, Manual mixing and application, Spraying out of pressure pots
• Lamination Process - Manual lamination, Membrane lamination, Press lamination, Vacuum lamination
• Product is free of Aromatic solvents
• For the bonding of genuine leather, artificial leather and spacer fabrics a double side adhesive application on the laminate and on the carrier is necessary to achieve the maximum bonding performance. For foil applications a single side adhesive application on the carrier is sufficient.
• Appropriate application methods are specified in the additional properties section of this document.
• A good starting point for the coating weight is approx. 150 - 200 g/m² wet on the carrier and approx. 150 - 250 g/m² wet on the flexible laminate. The final coating weights must be checked on the original substrates as they depend on the requirements and the behaviour of the bonding partners. 

Features

Ready-to-Use Product Features

Good Adhesion,

Good Bonding Strength,

Heat Resistance,

High Hydrolytic Stability

Features & Benefits

Labeling Claims

Aromatic Solvents-free,

Solvent-free

Product Benefits

• High initial bonding strength
• High heat resistance
• Good hydrolysis stability
• Very good adhesion

Packaging & Availability

Regional Availability

• Global

Storage & Handling

Storage Information

• Swift®col 2607-2A should be used within the shelf life specified on the packaging.
• The storage stability applies to material stored under appropriate conditions only (original unopened containers, recommended storage temperature).