Rakoll® 5010A

• high initial strength
• long open time
• excellent adhesion on various plastics
• high thermal stability
• good flexibility after complete curing
• label-free due to residual monomer content < 0.1 %

Pre-treatment of bonding surfaces:

• Bonding surfaces have to be clean, dry and free of grease and oil.
• Polyolefin materials have to be corona-pre-treated or flame-treated.

Preparation:

• Drum unloader, heating plate and applicator gun can, as a rule, be set to different temperatures.
• Excessive heat may cause decomposition of the adhesive.
• Depending on the construction of the equipment, a temperature of 110°C is enough for the heating plate.
• Due to the short operation time, the application equipment may be run at temperatures of up to 140°C.
• For tank melters only protective gasses with <5ppm humidity should be used.
• Positive results have been achieved with nitrogen.
• Please take care of that packages are used immediately after opening to prevent possible reactions with moisture.

Adhesive application:

• It is either applied in beads or tapes or as a sheet onto one of the bonding surfaces.
• Bonding is carried out immediately upon application.

Special attention:

• Final cure is achieved by reaction with ambient moisture or moisture from the substrate.
• Curing time depends on the access of humidity to the bonding seam, i.e. the humidity of the substrate, substrate permeability, adhesive film thickness, relative air humidity and ambient temperature.
• Average curing time for bonding onto wooden materials at a temperature of +20°C and relative humidity of 65% amounts to up to 3 – 4 days.
• If large surfaces and/or impermeable materials are bonded under unfavorable climatic conditions, the curing time maybe considerably longer.

Pre-treatment of bonding surfaces:

• Bonding surfaces have to be clean, dry and free of grease and oil.
• Polyolefin materials have to be corona-pre-treated or flame-treated.

Preparation:

• Drum unloader, heating plate and applicator gun can, as a rule, be set to different temperatures.
• Excessive heat may cause decomposition of the adhesive.
• Depending on the construction of the equipment, a temperature of 110°C is enough for the heating plate.
• Due to the short operation time, the application equipment may be run at temperatures of up to 140°C.
• For tank melters only protective gases with <5ppm humidity should be used.
• Positive results have been achieved with nitrogen.
• Please take care of that packages are used immediately after opening to prevent possible reactions with moisture.

Adhesive application:

• It is either applied in beads or tapes or as a sheet onto one of the bonding surfaces.
• Bonding is carried out immediately upon application.

Special attention:

• Final cure is achieved by reaction with ambient moisture or moisture from the substrate.
• Curing time depends on the access of humidity to the bonding seam, i.e. the humidity of the substrate, substrate permeability, adhesive film thickness, relative air humidity and ambient temperature.
• Average curing time for bonding onto wooden materials at a temperature of +20°C and relative humidity of 65% amounts to up to 3 – 4 days.
• If large surfaces and/or impermeable materials are bonded under unfavourable climatic conditions, the curing time maybe considerably longer.

• In original sealed packaging protected from sun, dust, moisture and high temperatures.
• Clean and dry conditions above -25°C and below +35°C.