H.B. Fuller MP5405FLEXMV

H.B. Fuller MP5405FLEXMV is a two-part unfilled rubber modified medium viscosity epoxy adhesive designed for high-speed bonding of metals, ceramics, and most plastics. It cures to a tough, semi-rigid material that is free-flowing in viscosity. It has good resistance to water, salt spray, inorganic acids and bases, and most organic solvents. It was specially formulated to a 1:1 mix ratio for use in either MMD equipment or side-by-side dual cartridges for easy dispensing. A handling cure is normally achieved at room temperature within 20 - 30 minutes, with full cure in 24 hours. An elevated temperature cure schedule can be used to reach final properties quickly.

Chemical Family: Epoxy & Epoxy Derivatives

Product Type: 2K (2 component) Adhesive, Epoxy Adhesive, Reactive Adhesive, Structural Adhesive

Compatible Substrates & Surfaces: Ceramic, Composites, Elastomers & Rubbers, Glass, Metal, Plastics, Wood

Features: Excellent Salt Spray Resistance, Free Flowing, Good Adhesion, Good Toughness, Medium Viscosity, Room Temperature Curing, Solvent Resistance

Technical Data Sheet

Enhanced TDS

Identification & Functionality

Chemical Family
Epoxy & Epoxy Derivatives
Product Type
2K (2 component) Adhesive,
Epoxy Adhesive,
Reactive Adhesive,
Structural Adhesive
Technologies
Adhesives & Sealants
Product Families
Adhesives & Sealants — Bonding Technology
2K Liquid Reactive Adhesives
Adhesives & Sealants — Functional Adhesives
Structural Adhesives

Features & Benefits

Ready-to-Use Product Features
Excellent Salt Spray Resistance,
Free Flowing,
Good Adhesion,
Good Toughness,
Medium Viscosity,
Room Temperature Curing,
Solvent Resistance

Applications & Uses

Markets
Automotive & Transportation,
Industrial
Applications
Industrial — Chemical & Industrial Manufacturing
Equipment & Parts
Automotive & Transportation — Transportation
Marine
Compatible Substrates & Surfaces
Ceramic,
Composites,
Elastomers & Rubbers,
Glass,
Metal,
Plastics,
Wood
General Instructions
  • Surfaces to be bonded must be clean, dry and free of other contaminants.
  • Bring both components to room temperature prior to mixing.
  • Measure out specified amounts of parts A and B and stir (without introducing bubbles) until homogenous or use a static mixing nozzle.
  • Apply the uniform mixture to both surfaces.
  • Allow to cure while being held in place with light clamping.

Properties

Color (Properties)
Transparent
Physical Form
Liquid
Appearance
Clear liquid
Component A
ValueUnitsTest Method / Conditions
ViscosityPaste--
Component B
ValueUnitsTest Method / Conditions
Viscosity15000.0cP-
Cured Properties
ValueUnitsTest Method / Conditions
Hardness79.0-ASTM D2240
Tensile Strength45.5MPaASTM D638
Elongation at Break5 - 10%ASTM D638
Operating Temperature- 40 - 130°C-
Dielectric Constant (at 100Hz)4.5-ASTM D150
Dielectric Strength16.1kV/mmASTM D149
Uncured Properties
ValueUnitsTest Method / Conditions
Specific Gravity (Part A)1.11--
Specific Gravity (Part B)1.15--
Specific Gravity (Mix)1.13--
Volume Mix Ratio1:1--
Pot Life (20 gram)3 - 5min-
Handling Time Full Cure (at 23°C)20 - 30min-
Handling Time Full Cure (at 66°C)24.0h-
Rheological Properties
ValueUnitsTest Method / Conditions
Viscosity (Mixed)Paste--

Packaging & Availability

Regional Availability
  • Latin America
  • North America

Storage & Handling

Shelf Life
12 Months
Storage Conditions
  • Product should be stored in a cool and dry place out of direct sunlight.
  • The shelf life is from date of manufacture.
  • Shelf life is based on the products being stored properly at temperatures between 12°C and 25°C.
  • Exposure to temperatures above 25°C will reduce the shelf life.
  • This product should not be frozen.