Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Product Families
Features & Benefits
- Ready-to-Use Product Features
- Features and Benefits
- Can cure at room temp with P13115 primer
- Good adhesion to glass, many plastics and metals
- Flexible after cure
Applications & Uses
- Markets
- Applications
- Compatible Substrates & Surfaces
- Cure Method
- Instruction for Use
1. Prior to bonding, surfaces must be free of any dust, oils, or other contaminants.
2. A UV lamp with a wavelength of 365nm is required; the UV light should be focused on the coated surface.
3. Curing speed is determined by the intensity of UV radiation, the distance from the UV light source and the coating surface. The depth of coating material can also affect cure time.
4. Immediately close the lid after use. A black hose must be used to dispense the adhesive.
5. This material should be stored away from sunlight, UV light and artificial light sources.
Properties
- Color (Properties)
- Uncured Properties
Value Units Test Method / Conditions Viscosity 18020.0 cP - Density 1.09 g/cm³ - Thixotropic Index 4.1 - - Surface Tack-Free Time (at 100 mW/cm²) max. 10 s - Depth of Cure (at 24sec) 6.0 mm - - Typical Cured Properties
Value Units Test Method / Conditions Hardness (100 mW/cm², at 365 nm, 24s) 62.0 - Shore D Tensile Strength (at Break, 100 mW/cm², at 365 nm, 24s) 19.6 MPa - Elongation at Break (100 mW/cm², at 365 nm, 24s) 139.0 % - Young’s Modulus (100 mW/cm², at 365 nm, 24s) 333.7 MPa - Glass Transition Temperature (100 mW/cm², at 365 nm, 24s) 52.3 °C - Lap Shear Strength (Polycarbonate, 100 mW/cm², at 365 nm, 24s) 7.2 MPa - Lap Shear Strength (Glass - Aluminum, 100 mW/cm², at 365 nm, 24s) 9.5 MPa - Surface Resistivity (100 mW/cm², at 365 nm, 24s) 8.0 x 10¹⁴ ohm - Volume Resistivity (100 mW/cm², at 365 nm, 24s) 8.0 x 10¹⁴ ohm - Dielectric Breakdown Strength (100 mW/cm², at 365 nm, 24s) 22.0 kV/mm - Dielectric Constant (at 1MHZ, 100 mW/cm², at 365 nm, 24s) 4.2 - - Dissipation Factor (at 1MHz, 100 mW/cm², at 365 nm, 24s) 0.03 - - Fixture Time (One side with P13115, 25°C for 24 hours) 4.0 min - Lap Shear Strength (Aluminum, One side with P13115, 25°C for 24 hours) 15.7 MPa - Cure Energy 2400.0 mJ/cm² -
Technical Details & Test Data
- Cure Conditions
- 100mW/cm² @ 365nm for 24s +
- One side with P13115 primer, 25C for 24hrs
- 80°C for 90min
- 120°C for 60min
Packaging & Availability
- Regional Availability
Storage & Handling
- Shelf Life
- 6 Months
- Storage Conditions
EA6201 should be sealed and stored in original container between 8ºC and 28ºC in a dry, dark place.
Shelf life at these conditions is 6 months from date of manufacture.