Fast-Setting Epoxy can be used to repair tools, auto parts, electrical and electronic components, furniture and other applications that require a fast-setting adhesive. Surface must be clean and dry before application. Remove all chemicals, dirt, wax and oil. To obtain the best cured properties, accurate proportioning and thorough mixing are essential.
Properties
- Color (Properties)
- Physical Form
- Component A
Value Units Test Method / Conditions Viscosity 465000.0 cP - - Component B
Value Units Test Method / Conditions Viscosity 400000.0 cP - - Cured Mechanical Properties
Value Units Test Method / Conditions Overlap Shear Strength (30 min, Aluminum, acid etched at 25°C) 717.0 psi - Overlap Shear Strength (60 min, Aluminum, acid etched at 25°C) 1700.0 psi - Overlap Shear Strength (15 min, Aluminum, acid etched at 25°C) 346.0 psi - Elongation at Break 8.5 % ASTM D638 Hardness 83.0 - ASTM D2240 Tensile Strength 7250.0 psi ASTM D638 Overlap Shear Strength (Aluminum, acid etched at -40°C, at 50% RH) 830.0 psi ASTM D1002 Overlap Shear Strength (Aluminum, acid etched at 25°C, at 50% RH) 3712.0 psi ASTM D1002 Overlap Shear Strength (Aluminum, acid etched at 82°C, at 50% RH) 425.0 psi ASTM D1002 Overlap Shear Strength (Aluminum, acid etched at 149°C, at 50% RH) 174.0 psi ASTM D1002 T-Peel Strength (at 82°C, acid etched Al-Al) 2.0 pli - T-Peel Strength (Acid etched Al-Al) 2.7 pli - T-Peel Strength (at -40°C, acid etched Al-Al) 1.0 pli - Operating Temperature 82.0 °C - - Uncured Properties
Value Units Test Method / Conditions Specific Gravity (Mix) 1.17 - - Specific Gravity (Part A) 1.19 - - Specific Gravity (Part B) 1.15 - - Gel Time (at 25°C, 4 gram) 3 - 5 min - Handling Time 15 - 30 min - Full Cure (at 23°C) 24.0 h - - Rheological Properties
Value Units Test Method / Conditions Viscosity (Mixed) Thixotropic paste - -
Storage & Handling
- Shelf Life
- 24 Months
- Storage Conditions
These materials should be stored in a dry environment within a temperature range of 16 °C to 27 °C (60°F to 80 °F). Extremes of temperature beyond this range may result in crystallization or polymerization of the materials. Introduction of a nitrogen blanket into the containers before closing will improve the storage life of the products.