Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Markets
- Applications
- Application Area
- Compatible Substrates & Surfaces
- Cure Method
- Curing Conditions
Cure speed will vary with temperature, relative humidity, depth of material and presence of moisture. Some applications may require special surface preparation. At 21 - 25°C, 45 - 55% relative humidity, typical cure depth is 2mm in 24 hours. Requires more time to cure in colder or lower humidity conditions.
- General Instructions
- For best performance bond surfaces should be clean, dry and free of any contaminants and oils.
- Apply a continuous and even bead of silicone to one surface.
- Assemble parts immediately. Remove excess material at once.
Properties
- Color (Properties)
- Physical Form
- Appearance
- White thixotropic paste
- Technical Data
Value Units Test Method / Conditions Specific Gravity 2.6 - - - Cured Properties
Value Units Test Method / Conditions Lap Joint Shear Strength (Aluminum, 50% RH) 1.5 MPa GB/T 7124 Elongation at Break (50% RH) 180.0 % GB/T 528 Hardness 82.0 - GB/T 531, Shore A Tensile Strength (50% RH) 3.5 MPa GB/T 528 Thermal Service Range - 54 - 210 °C - - Uncured Properties
Value Units Test Method / Conditions Tack Free Time 3.0 min - Full Cure Time (min. 2mm) 24.0 h - - Rheological Properties
Value Units Test Method / Conditions Viscosity Thixotropic paste - -
Packaging & Availability
- Regional Availability
Storage & Handling
- Storage Condition
Product shall be ideally store in a cool, dry area in unopened containers. Material should be stored at a temperature of 5 - 25°C and shelf life is a one year in original unopened containers.