Ködisil 110T

Identification

Chemical Family

Silicones

GBU

BAS

RTU Product Type

1K (1 component) Sealant,

1K (1 component) Adhesive,

Reactive Sealant,

Reactive Adhesive

Categories

Markets → Automotive & Transportation → Applications → Transportation → Off Road & Recreational Vehicle (RV)

Markets → Building & Construction → Applications → Building Materials → Construction Adhesives

Technologies → Adhesives & Sealants → Product Families → Bonding Technology → 1K Liquid Reactive Adhesives

Technologies → Adhesives & Sealants → Product Families → Sealing Technology → Reactive Sealants

Application Information

Cure Method

Moisture Cure

Applications

Application Area

Windows,

Recreational Vehicles,

HVAC Applications

Compatible Substrates & Surfaces

Ceramic,

Glass,

Metal,

Plastics,

Wood,

Steel,

Stone,

Concrete,

Aluminum Alloys

Applications & Uses

Application Information

Applications	Fields of Application	Construction industrial assembly
	Special Applications	Especially suitable for RV (recreational vehicle) assembly
Processing	Suitable Substrates	Various aluminum alloys
		Various steel alloys
		Many thermoplastics (except PMMA)
		Thermosetting plastics
		Glass
		Concrete
		Stone
		Various ceramics
		Wood
		Various other substrates
	Consistency	Pasty
	Surface Requirements	Dry
		Clean
		Free of grease
		Free of dust
	Adhesion Promoter (absorbing surface)	Körabond HG 92
	Adhesion Promoter (non absorbing surface)	Körabond HG 78
Cleaning	Cleaner for Tools	Körasolv Silicone

Cleaning Instructions

Clean tools immediately after use. Once cured, the material can only be removed mechanically. Appropriate cleaners are listed in the product properties.

Preparation

For some substrates the use of mechanical pretreatment and/or cleaner or primer is necessary to achieve good adhesion. Refer to the product properties section of this data sheet for special surface requirements and suitable adhesion promoters. Due to the huge variety of available substrates preliminary testing regarding adhesion and compatibility is strongly recommended.

Processing

Low temperatures can cause a temporary increase in viscosity resulting in reduced extrusion and slower curing rates.

Features

Ready-to-Use Product Features

Excellent UV Stability,

Exceptional UV Resistance,

Good Sagging Resistance,

Good Weather Fastness,

High Elasticity

Packaging & Availability

Regional Availability

• North America

Physical Properties

Color (Properties)

Transparent

Physical Form

Paste

Properties

Density:

1010 kg/m³

Specific Gravity:

1.01

Tensile Strength:

1.1 MPa

Recommended Operating Conditions

	Value	Units	Test Method / Conditions
Nominal Service Temperature	-40 to 180	°C	-

Physical Properties

	Value	Units	Test Method / Conditions
Density	1.01	g/cm³	DIN EN 542

Cured Properties

	Value	Units	Test Method / Conditions
Hardness (after 28 days, thickness of specimen = 6 mm)	20	Shore A	DIN ISO 7619-1
Joint Movement Capability	25	%	-
Skin Forming Time	8	minutes	Kö-test method 100109
Tensile Strength	1.1	MPa	DIN EN ISO 527

Processing Parameters

	Value	Units	Test Method / Conditions
Processing Temperature	10 - 30	°C	-
Required Squeezing Pressure	2	bar	-

Typical Properties

	Value	Units	Test Method / Conditions
Base	Silicone rubber	-	-
Storage Temperature	15 - 25	°C	-

Storage & Handling

Storage Conditions

Ködisil 110T should be used within the shelf life specified on the packaging. The storage stability only applies to material stored in original unopened containers, at storage temperature -15°C to 25°C.