H.B. Fuller UR4515GF

Identification

Chemical Family

Polyurethanes (PU)

GBU

EA

RTU Product Type

2K (2 component) Adhesive,

Reactive Adhesive,

Structural Adhesive

Categories

Markets → Industrial → Applications → Chemical & Industrial Manufacturing → Industrial Adhesives & Sealants

Markets → Industrial → Applications → Maintenance, Repair & Overhaul

Technologies → Adhesives & Sealants → Product Families → Bonding Technology → 2K Liquid Reactive Adhesives

Technologies → Adhesives & Sealants → Product Families → Functional Adhesives → Structural Adhesives

Applications

Compatible Substrates & Surfaces

Metal,

Plastics,

Polycarbonate (PC),

Polyethylene (PE)

Applications & Uses

General Instructions

Surfaces to be bonded must be clean, dry and free from grease, oil, wax, weak oxide films and other contaminants. Bring both components to room temperature prior to mixing. Measure out specified amounts of parts A and B and mix, without introducing bubbles, until homogenous. Meter-mix equipment equipped with an automatic purge is recommended for higher volume applications. Contact your H.B. Fuller representative for suggested application equipment to suit your specific needs. We recommend that containers be purged with nitrogen after they are opened to the air and not all the material is used.

Features

Ready-to-Use Product Features

Abrasion Resistant,

Chemical Resistant,

Fast Curing,

High Performance,

Impact Resistance,

Solventless,

Thixotropic,

High Lap Shear Strength,

Easy To Apply,

Electrically Non Conductive,

Room Temperature Curing

Features & Benefits

Labeling Claims

Plasticizer-free,

Solvent-free,

Low VOC,

Non-Corrosive

Features & Benefits

• No solvents, plasticizers, or low volatile components
• Fast curing
• 1:1 mix ratio by volume, designed for easy use with automated dispense systems
• Excellent moisture penetration seal
• Extreme environmental and abrasion resistance
• Room temperature curing, no heat required
• Non-conductive, non-corrosive
• Outstanding chemical resistance
• High impact strength
• Will not induce stress cracking in polycarbonate or polyethylene parts

Packaging & Availability

Regional Availability

• Asia Pacific

Physical Properties

Color (Properties)

Green

Physical Form

Liquid

Properties

Density:

1250 kg/m³

Specific Gravity:

1.25

Viscosity:

90000 cps

Uncured Properties

	Value	Units	Test Method / Conditions
Full Cure (at 23°C, full uncured)	2 - 3	days	-
Full Cure (at 70°C, full uncured)	1 - 2	hours	-
Gel Time (at 23°C, 100g)	4	minutes	-
Mix Ratio (by volume)	1:1	-	-
Mix Ratio (by weight)	100:84	-	-
Specific Gravity	1.25	-	-

Cured Properties

	Value	Units	Test Method / Conditions
Elongation at Break (at 25°C, 50% RH)	57	%	ASTM D638
Hardness	80	Shore D	ASTM D2240
Overlap Shear Strength (at 25°C, 50% RH, aluminum, abraded)	2760	psi	ASTM D1002
Overlap Shear Strength (at 50% RH, E-Coat steel, IPA wipe)	20.05	MPa	ASTM D1002
Overlap Shear Strength (at 50% RH, nylon 6-6, abraded)	5.8	MPa	ASTM D1002
Overlap Shear Strength (at 50% RH, stainless steel, abraded cured)	14.9	MPa	ASTM D1002
Tensile Strength (at 25°C, 50% RH)	13.9	MPa	ASTM D638

Typical Properties

	Value	Units	Test Method / Conditions
Storage Temperature	16 - 25	°C	-

Component B

	Value	Units	Test Method / Conditions
Viscosity	5000	cPs	-

Component A

	Value	Units	Test Method / Conditions
Viscosity	90000	cPs	-

Storage & Handling

Storage

Product should be stored in a cool dry place out of direct sunlight. The shelf life is from date of manufacture. Shelf life is based on the products being stored properly at temperatures between 16°C and 25°C. Exposure to temperatures above 25°C will reduce the shelf life. This product should not be frozen. Purge opened containers with dry nitrogen inert blanketing gas before resealing.

Shelf Life

12 months