Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Product Families
Features & Benefits
- Ready-to-Use Product Features
- Product Highlights
- Optimum adhesion to glass, metal, stone, etc.
- Material will not sag and run after dispensing.
- Will not change or affect substrate appearance after cure.
- Excellent flexibility.
- Low odor, non-corrosive.
Applications & Uses
- Markets
- Applications
- Application Area
- Compatible Substrates & Surfaces
- Cure Method
- General Instructions
- For best performance, bond surfaces should be clean, dry, and free of any contaminants and oils.
- Apply a continuous and even bead of silicone to one surface, surrounding all bolt holes.
- Assemble parts immediately. Remove excess material at once.
- Fully cures (2mm) in 24 hours at 23±2°C, 50±5% relative humidity. More time may be needed to cure in colder or lower humidity conditions.
Properties
- Color (Properties)
- Appearance
- Transparent thixotropic paste
- Technical Data
Value Units Test Method / Conditions Specific Gravity 1.0 - - Tack Free Time min. 5 - - Full Cure Time 24 hours - Thermal Service Range -54 to 210 ºC - Hardness (Shore A) 25 - ASTM D638 Tensile Strength (at 23±2°C, 50% RH) 1.15 MPa ASTM D2240 Elongation to Break (at 23±2°C, 50% RH) 450 % ASTM D638 - Curing Conditions
Cure speed will vary with temperature, relative humidity, depth of material and presence of moisture. Some applications may require special surface preparation.
Packaging & Availability
- Regional Availability
Storage & Handling
- Storage Conditions
H.B. Fuller SN2310T shall be ideally store in a cool, dry area in unopened containers. Material should be stored at a temperature of 5- 25oC for a maximum shelf life of 1 year in the original unopened container. Do not return unused material back into the container.