Cilbond® 33C A/B
1 of 12 products in this brandRTU Product Type: 2K (2 component) Adhesive, Solventborne Adhesive
Application Area: Gaskets, Hoses, Oil Seals, Rollers, Shaft Seals, Valve Seals
Compatible Substrates & Surfaces: Fabrics, Fluoroelastomer (FKM), Metal, Thermoplastics
Application Method: Brush, Dip Coating, Spray
Features: Brake Fluids Resistant, Diluted Acid Resistant, Diluted Alkali Resistant, Excellent Performance, Good Glycol Resistance, Good Lubricant Resistance, Good Solvent Resistance, Heat Resistance, High Temperature Performance, High Temperature Resistance, Solvent-Based, Transmission Oil Resistance
-
Type Document Name
-
Technical Data SheetCilbond® 33C A/B Technical Data Sheet
Enhanced TDS
Identification
- Carrier
- GBU
- RTU Product Type
- Categories
Applications
- Application Area
- Application Method
- Compatible Substrates & Surfaces
- Segment
Applications & Uses
- Usage Information
-
Mixing: Cilbond 33A / 33B should be mixed in equal parts by volume and then thoroughly stirred, adding diluent as necessary. The two liquids mix readily within one or two minutes and the resulting mixture is an amber colour with no undissolved particles at ambient temperature. The solids content of the undiluted mix is ca. 32% and the mixture is stable for at least 4 days at ambient temperature, but should be used within one week of mixing.
Brushing: Cilbond 33A / 33B can be applied by brush.
Spraying: Cilbond 33A / 33B can be spray-coated. Ideally use an HVLP system with a 0.04–0.06 in (1–1.5mm) nozzle, using air-pressure of ≤22 psi (≤1.5 bar) and fluid pressure of ca. 7 psi (0.5 bar).
Dipping: Cilbond 33A / 33B can be dip-coated.
Dilution: Because of the high solids content, it may be necessary to dilute to achieve the required coating thickness. In most cases MEK or MIBK are the preferred diluents.
Uniform Coating: One or two coats should be used, dependent upon the surface texture of the substrate.
Coating thickness: A minimum dry film thickness of 0.2 mil (5 micron) is required for thin rubber sections as used in seals / gaskets. For thicker rubber sections use 0.6 mil (15 micron) dry coatings.
Drying: Coated components should be left to air-dry for 20 – 30 minutes at room temperature. Force drying the coated parts in an oven at 140°F for 10 minutes will speed up drying parts. Pre-warming parts to ~140oF prior to coating will also speed up drying.
Storage: It is recommended that components are bonded within seven days of application of the bonding agent, although under controlled conditions parts may be stored for longer
periods.
Cleaning: A minimum cure schedule of at least 30 minutes at 300°F is recommended. Depending on the elastomer, cure schedules over the temperature range of 300-375ï‚°F should give optimum bonding properties. Cure schedules above 375°F or below 300°F may show deterioration of bonding quality.
Using Cilbond 33A / 33B At a Ratio of 3 : 2- For difficult to bond fluoroelastomers, such as Zytel and peroxide cured fluoroelastomers and fluorosilicones, use Cilbond 33A : 33B mixed at a ratio 3 : 2 by volume.
- ​​​​​​​Furthermore, using a 3 : 2 mix ratio improves the heat resistance of the bond and reduces attack by migratory ingredients emanating from the elastomer during long-term heat ageing.
​​​​​​​Where To Use Cilbond 33A/ 33B
For the bonding of all hardness grades of fluoroelastomer to substrates by compression or injection moulding. A minimum cure schedule of 30 minutes at 300°F is recommended to maximise adhesion and the environmental resistance of the bond.​​​​​​​
End use applications include- Oil-Seals
- Shaft Seals
- Gaskets
- Valve Seals
- Rollers
- Hoses
Features
- Ready-to-Use Product Features
Features & Benefits
- Product Benifits
-
Bonding Capabilities:
- Cilbond 33A / 33B is a two component adhesive system, which is mixed to produce a one-coat system.
- Cilbond 33A / 33B is suitable for bonding fluoroelastomer compounds of all hardnesses to a variety of substrates including metals (either chemically treated or mechanically abraded) and thermoplastics, thermosets and fabrics.
- The Cilbond 33A / 33B system will bond all the major grades of fluoroelastomers available including Viton®, Daiel®, Aflas®, Technoflon® and Fluorel®, which are bisphenol or amine cured and may also bond some peroxide cured fluoroelastomers and even some fluorosilicones, especially if post cured.
In-service Benefits:
- Cilbond 33A / 33B exhibits excellent resistance to high post-curing temperatures and harsh chemical environments including lubricants and transmission oils to 392°F, mild aqueous acid and mild alkalis to 212°F, solvents, brake fluids and glycols.
- The heat resistance of Cilbond 33A / 33B is excellent and will survive extended periods at above 392°F.
​​​​​Processing Benefits:
- Cilbond 33A / 33B may be pre-baked if required and a pre-bake of up to 10 minutes at 300°F or 30 minutes at 275°F is recommended. In certain cases a pre-bake may be a necessary part of the bonding procedure to prevent bonding agent wiping (i.e. melt flow of the adhesive).
Packaging & Availability
- Regional Availability
- Packaging Information
-
Cilbond 33A / 33B is supplied in 2 pint and 2.5 US Gallon containers. 1⁄2 pint trial samples are also available upon request.
Physical Properties
- Physical Form
- Appearance
-
Clear to amber liquid
Properties
- Typical Physical Properties
-
Value Units Test Method / Conditions Combined Solids 32 % - Flash Point -8 °C Abel Pensky Method Pot Life of Combined System (combined system) 4 - 7 days - Recommended Dry Coating Thickness (5 microns) 0.2 mil/5microns - Typical Coverage approx. 1225 - 1425 ft/gal - Viscosity 15 seconds - - Component A
-
Value Units Test Method / Conditions Combined Solids 32 % - Combined Viscosity 16 seconds No. 2 Zahn Cup Density 8.1 lbs/gal - Non-Volatile Solids 43 Wt(%) - Pot Life of Combined System 4 - 7 days - Recommended Dry Coating Thickness 0.2 mil/5microns - Specific Gravity 0.97 - - Viscosity 16 seconds No. 3 Zahn Cup Volatile Organic Compound Content 57 Wt(%) - Volume Solids 38.4 % - - Component B
-
Value Units Test Method / Conditions Combined Viscosity 16 seconds - Density 7.3 lbs/gal - Non-Volatile Solids 22 Wt(%) - Specific Gravity 0.88 - - Volatile Organic Compound Content 78 Wt(%) - Volume Solids 19.1 % - - Appearance
-
Clear to amber liquid
Regulatory & Compliance
- Certifications & Compliance
Storage & Handling
- Shelf Life
-
24 months