H.B. Fuller MP54110
1 of 79 products in this brandH.B. Fuller MP54110 is a two-part unfilled epoxy adhesive designed for bonding of metals, ceramics, and most plastics. This product gives good resistance to water, salt spray, inorganic acids and bases, and most organic solvents. This product has better water and temperature resistance than standard 5-minute epoxy. It was specially formulated to a 1:1 mix ratio for use in either MMD equipment or side-by-side dual cartridges for easy dispensing. A handling cure is normally achieved at room temperature within 30 - 60 minutes, with full cure in 24 hours. An elevated temperature cure schedule can be used to reach final properties quickly.
Chemical Family: Epoxy & Epoxy Derivatives
RTU Product Type: 2K (2 component) Adhesive, Epoxy Adhesive, Reactive Adhesive, Structural Adhesive
Application Area: Cartridge
Compatible Substrates & Surfaces: Ceramic, Metal, Plastics
Features: Excellent Salt Spray Resistance, Free Flowing, Good Adhesion, Good Mechanical Properties, Good Sagging Resistance, Good Toughness, Room Temperature Curing, Solvent Resistance
-
Type Document Name
-
Technical Data SheetH.B. Fuller MP54110 Technical Data Sheet
Enhanced TDS
Identification
- Chemical Family
- GBU
- RTU Product Type
- Categories
Applications
- Application Area
- Compatible Substrates & Surfaces
Applications & Uses
- General Instructions
-
- Surfaces to be bonded must be clean, dry and free of other contaminants.
- Bring both components to room temperature prior to mixing.
- Measure out specified amounts of parts A and B and stir (without introducing bubbles) until homogenous or use a static mixing nozzle.
- Apply the uniform mixture to both surfaces.
- Allow to cure while being held in place with light clamping.
Features
- Ready-to-Use Product Features
Packaging & Availability
- Regional Availability
Physical Properties
- Color (Properties)
- Physical Form
- Appearance
-
Clear liquid
Properties
- Viscosity:
-
20000 cps
- Cured Properties
-
Value Units Test Method / Conditions Hardness 80 Shore D ASTM D2240 Operating Temperature - 40 to 130 °C - Overlap Shear Strength (at 25°C, 50% RH, aluminum, acid etched) 15.9 MPa ASTM D1002 - Uncured Properties
-
Value Units Test Method / Conditions Handling Time Full Cure (at 23°C) 30 - 60 minutes - Handling Time Full Cure (at 66°C) 24 hours - Mix Ratio (by volume, ucnured) 1:1 - - Mix Ratio (by weight) 1:1 - - Pot Life (at 25°C, 20g) 8 - 12 minutes - Specific Gravity (mix) 1.16 - - Specific Gravity (part A) 1.17 - - Specific Gravity (part B) 1.15 - - - Typical Properties
-
Value Units Test Method / Conditions Elongation at Break 10 % - Open Time 10 minutes - Storage Temperature 12 - 25 °C - - Component A
-
Value Units Test Method / Conditions Viscosity 12000 cPs - - Rheological Properties
-
Value Units Test Method / Conditions Viscosity (at 25°C) 15000 cPs - - Component B
-
Value Units Test Method / Conditions Viscosity 20000 cPs - - Appearance
-
Clear liquid
Storage & Handling
- Storage Conditions
-
- Product should be stored in a cool and dry place out of direct sunlight.
- The shelf life is from date of manufacture.
- Shelf life is based on the products being stored properly at temperatures between 12°C and 25°C.
- Exposure to temperatures above 25°C will reduce the shelf life.
- This product should not be frozen.
- Shelf Life
-
12 months